Stiffness and strength of composite truss beam to R.C. column connection in MRFs
2015
Abstract The results of experimental and numerical investigations on the cyclic behavior of composite truss beam to reinforced concrete column connection of moment resisting frames are reported. The beams are constituted by a steel truss and end zone added rebar embedded within a concrete block cast in place, so that, after curing, the steel truss and the added rebar work together with the concrete matrix as reinforcement of the composite beam. Particularly, three specimens of two-span continuous beams were tested under monotonic and cyclic actions as three point bending test. With the goal to investigate about the behavior of the end zone of the beam integrated into a moment resisting fram…
A DIC-based study of flexural behaviour of roving/mat/roving pultruded composites
2015
Abstract This paper reports a study of the flexural behaviour and resultant failure modes in E-glass/polyester pultruded composites. The digital image correlation (DIC) method is used to estimate the effect of fibre orientation on failure behaviour in thick beams, taking into account the presence of continuous filament mat layer (CFM) in the stacking sequence. In particular, the tests were carried out for specimens with off-axis angle of 0°, 7.5°, 15°, 30°, 45° and 90°. The crack initiation and the failure mechanisms depend on the mutual interaction between the stiffness properties of different areas in the stacking sequence. An influence index (I) was introduced to evaluate the magnitude o…
Experimental assessment of the shield-to-salt-fog properties of basalt and glass fiber reinforced composites in cork core sandwich panels applications
2018
Abstract In this paper, the effect of salt-fog exposition on the mechanical behavior of sandwich panels having cork agglomerate core was investigated. In particular, the aim of this research work is to assess the shield function of unidirectional basalt and E-glass reinforced polymer on the aging and failure mechanism of the core when such class of material are destined to operate in hostile environments (e.g., marine environment). To do this, the manufactured sandwich panels were exposed up to 60 days to salt-fog environment, according to ASTM B 117 standard. Unaged and aged specimens were analyzed through three point bending tests after aging time of 10, 25 and 60 days. Digital Image Corr…
Flexural behaviour of external R/C steel fibre reinforced beam-column joints
2011
ABSTRACT A softened strut-and-tie macro model able to reproduce the flexural behaviour of external beam-column joint is presented. The model is specific for concrete with hooked steel fibres (FRC) and it is designed to calculate the flexural response, as load-deflection curve, of a beam-column sub-assemblages. The model considers the presence of a constant vertical load acting on the column and of a monotonically increasing lateral force applied at the tip of the beam.
Mechanical properties of sol–gel derived SiO2 nanotubes
2014
The mechanical properties of thick-walled SiO2 nanotubes (NTs) prepared by a sol–gel method while using Ag nanowires (NWs) as templates were measured by using different methods. In situ scanning electron microscopy (SEM) cantilever beam bending tests were carried out by using a nanomanipulator equipped with a force sensor in order to investigate plasticity and flexural response of NTs. Nanoindentation and three point bending tests of NTs were performed by atomic force microscopy (AFM) under ambient conditions. Half-suspended and three-point bending tests were processed in the framework of linear elasticity theory. Finite element method simulations were used to extract Young’s modulus values…
Bending test for capturing the vivid behavior of giant reeds, returned through a proper fractional visco-elastic model
2015
Abstract This paper presents results of experimental investigations made to evaluate the vivid behavior of giant reed Arundo donax. In particular, attention was paid to the relationship between visco-elastic properties and moisture content, which is widely recognized as one of the key factor that influences the mechanical properties of all wood-based materials. To this aim, after a controlled drying treatment on samples of reed, stress relaxation tests in three point bending configuration were performed to evaluate the effects of moisture content on visco-elastic behavior of the giant reed. Further, the novel aspect of this paper is that of using an Euler–Bernoulli model embedded with an ad…
Longitudinal Flexure as a Method for Determining the Flexural Strength of Composite Materials
2004
A method is presented for determining the flexural strength of composites from tests on pinned specimens in axial compression. This scheme is close to the so-called Euler buckling model, but the load is applied eccentrically, and the bar is bent practically from the beginning of loading. An analytical model is proposed for calculating the flexural stress in longitudinal flexure of a thin bar in the case of large displacements. The problem is solved in elliptic integrals of the first and second kinds. The analytical model shows an excellent agreement with experiments. The results obtained are compared with experimental tension data. A device is also designed for testing composite bars in lon…
Mechanical Behaviour of a Green Sandwich Made of Flax Reinforced Polymer Facings and Cork Core
2015
Abstract This work investigates the flexural behavior of a composite sandwich made of flax fibers reinforced skin facings and an agglomerated cork core, to be employed as an eco-friendly solution for the making of structural components of small sailing boats. An experimental mechanical characterization of the strength and stiffness flexural behavior of the proposed sandwich is carried out, providing a comparison of performances from three implemented assembling techniques: hand-lay-up, vacuum bagging and resin infusion. Sandwich beams have been tested under three point bending (TPB) at various span lengths. A procedure is also proposed and implemented to consider the potential influence of …
Salt-fog spray aging of jute-basalt reinforced hybrid structures. Flexural and low velocity impact response
2017
Abstract In this work, a study on the aging resistance of jute and jute-basalt interply hybrid laminates exposed to salt-fog is presented with the aim to investigate the possibility to enhance the durability of natural fiber reinforced composites for marine application by a ply-substitution approach. In particular, jute and basalt/jute reinforced composite plates were manufactured by vacuum assisted resin infusion in two different staking sequences (i.e., intercalated and sandwich-like basalt-jute) and aged under salt fog conditions. The effects of the accelerated aging at increasing times on the mechanical response of laminates were assessed in both quasi static (three point bending) and d…
Mechanical properties of pultruded glass fiber-reinforced plastic after moistening
2012
Abstract The kinetics of moisture sorption under immersion in water at room and elevated temperatures and flexural characteristics of dry (conditionally initial) and wet (moistened up to saturation level) composite material were investigated on flat specimens of polyester based glass fiber-reinforced plastic, cut from I-beam pultruded profile. It was found that the coefficients of diffusion and swelling are different in three principal axis of the composite. The former have the largest value in fiber axis direction, but the latter – in transverse to fiber axis direction out of plane of the layers. The observed difference in kinetics of mass gain and change of volume strain for the specimens…